0.7 La2O3 Molybdenum Lanthanum Alloy Utensil for Metal Sheet and Plate Sintering

0.7 La2O3 Molybdenum Lanthanum Alloy Utensil for Metal Sheet and Plate Sintering

Material: Molybdenum-lanthanum alloy (0.7% La2O3), mainly used to produce sheet and plate.

Density: 9.7g/cm³

Working temperature: about 2000 degree centigrade.

Joining method: riveted, folded and welded (per customer request, riveted boat is recommended)

Specification: According to customer’s requirement and drawing.

Advantages:

Compared to pure molybdenum:

• Higher Stability;
• Better Creep Resistance;
• Better Welding Performance.

Compared to TZM:

• Better Thermal Stability;
• Better Creep Resistance;
• Better Ductility in High Temperature.

SEM of molybdenum alloy after sintering.

Application:

Vacuum thermal evaporation air;

Capacitor sinter

Crust of thermocouple pit etc.

Mainly used as:

1. Sintering and annealing utensil for metal and nonmetal materials in reduction atmosphere.

2. Sintering utensil for powder products.

3. Heating Elements in High Temperature Furnace.

4. Heating Zone for Vacuum furnace (Electrical resistivity at 1200 degree centigrade is 0.374Ω mm/m²)

5. Heat Shield.

 Welcome check with Shanghai Rare Metal for your Rare Metal needs!